The number of double rubs is counted.
The extent of cure was measured by methyl ethyl ketone double rubs.
The number of double rubs needed to achieve this was recorded.
A method for measuring the acetone double rubs is described herein.
The number of double rubs which the film could sustain before deterioration resulted was recorded.
The results are expressed as the number of double rubs till removal of the coating.
Wet double rubs and pencil hardness measured 1 hour after application.
The film was subjected to double rubs with methyl ethyl ketone.
Wet double rubs measured 1 hour after treatment with TEOS.
The prints were stroked with ten double rubs to evaluate adhesion and durability.
After the coatings were prepared, they were tested for MEK double rubs.
These were tested for cure by resistance to double rubs with acetone as described below.
Acetone / ethanol double rubs A piece of cloth is soaked in the required solvent.
Chemical resistance and extent of cure was evaluated by double rubs using methyl ethyl ketone.
Acetone double rubs ( ADR ) were carried out as described herein to determine the curing.
See also
The number reported is the number of double rubs required to expose the metal surface.
The cloth was saturated with MEK after every twenty-five double rubs.
The reported number is the number of double rubs required to break through the coating.
The MEK double rubs are measured for films cured for 1 day at ambient temperatures.
The rag was redoused with the solvent every fifty double rubs across the coating surface.
MEK resistance - of MEK double rubs required to break through or significantly mar the coating.
Rather, the film dissolved after only 10 acetone double rubs were performed.
Wet double rubs and pencil hardness measured 24 hours after conditioning.
The cured coating was solvent resistant in that it withstood 100 acetone double rubs.
Wet double rubs and pencil hardness measured 24 hours after application.
Rubbing was discontinued if the primer was still intact after 100 double rubs was reached.
The film was unaffected by 100 double rubs with a rag soaked with methyl ethyl ketone.
The rubbing was continued until bare metal is observed or until 200 double rubs are completed.
Data were reported as MEK double rubs ( one set of back and forth ).
The bulk polyurethanes preferably demonstrate solvent resistance after 100 methyl ethyl ketone double rubs.
Values of less than 100 indicate the number of double rubs before the coatings was destroyed.
The cloth was resaturated with MEK after every 25 double rubs.
The coatings withstood 200 MIBK double rubs without significant marring.
The solvent resistance was determined by methyl ethyl ketone ( MEK ) double rubs.
The coatings passed 20 MIBK double rubs without marring but showed some dulling at 50 double rubs.
The 8th line gives the solvent resistance ( the number of double rubs with acetone ).
The cured coating survived 200 MEK double rubs and gave a particularly clear coating film.
The cure response was evaluated vÃa methyl ethyl ketone ( MEK ) double rubs.
Methyl ethyl Ketone ( MEK ) double rubs were measured as follows.
The swab remains soaked with MEK throughout the 50 double rubs.
The maximum cure speed and MEK double rubs after 1 hour are shown in Table 11.
The cured coating survived 80 MEK double rubs.
Greater than 100 double rubs is considered to be adequately cured.
This continuous thermoset coating had excellent chemical resistance, passing 150 double rubs with methyl ethyl ketone.
MEK double rubs were 50, which indicates good cure.
The systems were evaluated for cure using 200 double rubs with methyl ethyl ketone.
The solvent-resistance of the cured coating was greater than 200 MEK double rubs.
The finish withstands over 100 double rubs in a so-called double rub test.
The cured film was measured at more than 200 double rubs.
The results of the MEK double rubs tests were similar to those obtained for PUD 's 4-6.