Ring and ball softening range.
All softening points are measured using the ring and ball method.
Ring and ball temperature.
The softening point is usually determined by the ring and ball test method.
The ring and ball softening point is expressed in ° C.
These rupture temperatures are also determined by measuring the ring and ball softening temperature.
Ring and ball softening point is the reported values in accordance with ASTM E 28.
The test is often referred to as the Ring and Ball test.
A preferred asphalt has a ring and ball softening point higher than about 90°C.
A decrease in the butene-1 content causes an increase in the ring and ball softening point.
Preferably the asphalt has a ring and ball softening point higher than about 90°C.
Bitumen and bituminous binders - Determination of the softening point - Ring and Ball method.
Preferred are tackifiers having a Ring and Ball softening point above about 25°C.
The ring and ball softening point determination is carried out using ASTM E-28 test method.
Variable parameters - Ring and ball material.
See also
The ring and ball softening point determinations are carried out using ASTM E-28 test method.
The resulting resin was characterised by a Ring and Ball softening point of l25°C.
The ring and ball softening point may be measured by ASTM D36.
In another embodiment, the adhesive comprises a tackifier with a ring and ball softening point greater than 100°C.
The ring and ball softening point determination is done according to ASTM E28.
Those rosins preferred will have Ring and Ball softening points of at least 60°C.
The ring and ball softening point is typically measured according to ASTM D36.
Preferred are tackifying resin having a Ring and Ball softening point above about 25°C.
These tackifying resins have a ring and ball softening point from 70 degrees Celsius to 150 degrees Celsius.
Softening point, Softening point using the ring and ball method according to ASTM E28.
The resulting resin was characterised by a ring and ball softening point of 140°C.
Softening point was determined by the Ring and Ball method according to EN 1427.
The softening point was measured by the ring and ball method according to JIS K 2531.